稻壳灰的宏微观结构研究
作者：
龚晓强;刘杰胜;邢珊珊;董莪
期刊：
武汉轻工大学学报 ,2018年37(1):51-55 ISSN：2095-7386
作者机构：
武汉轻工大学土木工程与建筑学院 湖北武汉430023;[刘杰胜; 董莪; 邢珊珊; 龚晓强] 武汉轻工大学
关键词：
稻壳灰;制备;微观结构
摘要：
本文采用不同温度（400 ℃、600 ℃和800 ℃）对稻壳进行煅烧制备稻壳灰，结合扫描电子显微镜（SEM）表征手段，研究了不同煅烧温度对稻壳产灰率及宏微观结构的影响。试验结果得出：随着煅烧温度的升高，稻壳的产灰率逐渐降低；煅烧温度较高使得稻壳燃烧更充分，其表面结构呈现熔融收缩状，稻壳灰夹层呈现中空的状态。试验所得结论为提高农业的废弃物—稻壳的利用率、减少对环境的污染提供了新的思路，也为稻壳灰在建材中的进一步应用奠定一定的基础。
语种：
中文
展开
The Study of the Interaction between Silica Filler and Silicone Rubber
作者：
Liu, Jiesheng* ;Gong, Xiaoqiang;Zhang, Rongtang
作者机构：
[Liu, Jiesheng] Wuhan Polytech Univ, Guangxi Key Lab Rd Struct & Mat, Wuhan 430023, Hubei, Peoples R China.;[Liu, Jiesheng; Gong, Xiaoqiang; Zhang, Rongtang] Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan 430023, Hubei, Peoples R China.
会议名称：
5th Annual International Conference on Material Science and Environmental Engineering (MSEE)
会议时间：
DEC 15-17, 2017
会议地点：
Xiamen, PEOPLES R CHINA
会议主办单位：
[Liu, Jiesheng] Wuhan Polytech Univ, Guangxi Key Lab Rd Struct & Mat, Wuhan 430023, Hubei, Peoples R China.^[Liu, Jiesheng;Gong, Xiaoqiang;Zhang, Rongtang] Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan 430023, Hubei, Peoples R China.
会议论文集名称：
IOP Conference Series-Materials Science and Engineering
摘要：
The interaction between silica filler and silicone rubber was studied by swelling ratio, Kraus curve and crosslinking density test. The results showed that lower values of Vro/Vrf and swelling ratio in modified filler system suggests good filler-matrix interactions. The composites with silane coupling agents show higher crosslink-density compared that of untreated ones. In the light of the above statement, it can be concluded that modification of filler is the crucial factor in creating a good interaction between the filler and silicone rubber.
语种：
英文
展开
改性剑麻纤维对水泥砂浆的性能研究
作者：
段焱侠;董莪;李发平;刘杰胜;高璇
期刊：
武汉轻工大学学报 ,2018年37(3):60-63+97 ISSN：2095-7386
作者机构：
武汉轻工大学 土木工程与建筑学院,湖北 武汉,430023;[刘杰胜; 李发平; 董莪; 高璇; 段焱侠] 武汉轻工大学
关键词：
剑麻;改性纤维;水泥砂浆;硅烷偶联剂;力学性能
摘要：
笔者通过用硅烷偶联剂对剑麻纤维进行改性,并研究了改性剑麻纤维长度和质量分数对水泥砂浆的抗压强度、抗折强度、稠度和湿密度四个指标的影响。试验结果表明：掺入长度1 cm质量分数为1%的改性剑麻纤维,对试块的抗压强度影响最大,较空白组抗压强度提高了27%。随着改性剑麻纤维的长度和质量分数的增加,水泥砂浆的抗折强度整体呈下降趋势。改性剑麻纤维长度为1 cm,质量分数为0.2%、0.5%时,较空白组抗折强度分别提高了1.06%和3.40%。改性剑麻纤维长度为3 cm、5 cm时,整体上抗折强度值均小于空白组水泥砂浆的抗折强度值。改变改性剑麻纤维质量分数与改变其长度相比,前者对水泥砂浆稠度的影响更大。且改性剑麻纤维水泥砂浆的湿密度随改性剑麻纤维长度的增大而减小,随改性剑麻纤维的质量分数增大而减小。
语种：
中文
展开
内掺有机硅改性防水砂浆的基本性能研究
作者：
李发平;刘杰胜;刑珊珊;余媛媛
期刊：
中国建筑防水 ,2017年(8):5-8 ISSN：1007-497X
作者机构：
武汉轻工大学土木工程与建筑学院,湖北武汉,430023;[刘杰胜; 李发平; 余媛媛; 刑珊珊] 武汉轻工大学
关键词：
防水砂浆;有机硅;密度;抗压强度;抗渗性能;耐化学腐蚀性
摘要：
内掺不同种类和不同含量的有机硅对水泥砂浆进行改性制成防水砂浆,研究了有机硅对防水砂浆基本性能的影响。结果表明,与普通水泥砂浆相比,内掺有机硅的防水砂浆密度减小、抗压强度减小,但抗渗性能和耐化学腐蚀性能得到了改善。
语种：
中文
展开
稻壳灰水泥砂浆环境影响评价
作者：
邢珊珊;董莪;刘杰胜;余媛媛;左洁
期刊：
武汉轻工大学学报 ,2017年36(1):61-66 ISSN：2095-7386
作者机构：
武汉轻工大学土木工程与建筑学院,湖北 武汉,430023;[刘杰胜; 左洁; 余媛媛; 董莪; 邢珊珊] 武汉轻工大学
关键词：
生命周期评价方法;稻壳灰水泥砂浆;能源消耗
摘要：
采用生命周期评价方法,对普通水泥砂浆和稻壳灰水泥砂浆的生产和使用阶段对环境的影响负荷进行分析。结果表明,稻壳灰水泥砂浆中稻壳灰取代部分水泥,水泥的用量减少,石灰石消耗值ADP也随之减少,同时,稻壳灰作为农业生产的废弃物再次被使用,所需的能源消耗相对于水泥较低。
语种：
中文
展开
Preparation and characterization of a microemulsion via polycondensation of alkoxyl silane
作者：
Liu Jiesheng* ;Gong Xiaoqiang;He Xiang;Zhang Rongtang
期刊：
RSC Advances ,2017年7(87):55360-55363 ISSN：2046-2069
通讯作者：
Liu Jiesheng
作者机构：
[Liu Jiesheng; He Xiang; Zhang Rongtang; Gong Xiaoqiang] Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan 430023, Hubei, Peoples R China.
通讯机构：
[Liu Jiesheng] W;Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan 430023, Hubei, Peoples R China.
摘要：
A microemulsion was successfully prepared via polycondensation of alkoxy silanes. Research into the control of the preparation and properties of the microemulsion was conducted. The structure and properties of the microemulsion were characterized by transmission electron microscopy (TEM) and photon correlation spectroscopy (PCS). The variation in the temperature, the methods, and the amount of catalyst and surfactant was studied in relation to the properties of the final microemulsion.
语种：
英文
展开
整体刚性自防水砂浆抗冻融性能研究
作者：
李发平;刘杰胜;杜立伟;董莪;邢珊珊
期刊：
武汉轻工大学学报 ,2017年36(1):71-76 ISSN：2095-7386
作者机构：
武汉轻工大学土木工程与建筑学院;[杜立伟] 武汉市东西湖区吴家山第一中学;[刘杰胜; 李发平; 邢珊珊; 董莪] 武汉轻工大学
关键词：
有机硅;水泥砂浆;抗冻
摘要：
随着我国的土木建筑业的不断发展,水泥砂浆起着举足轻重的作用.通过在普通水泥砂浆中加入不同掺量的有机硅来研究其对水泥砂浆的抗冻融性能的影响.研究表明内掺不同掺量有机硅聚合物水泥砂浆(SPM,Silicone Polymer Mortar)与普通水泥砂浆(M, Cement Mortar)在冻融条件下相比,内掺不同掺量有机硅聚合物水泥砂浆的质量损失率减少,强度损失率增大外观剥落情况良好.当发生冻融破坏时,有机硅与水发生反应,产生化学"偶联桥键"作用,使得界面作用增强, 导致质量损失率降低.
语种：
中文
展开
Silane Treatment Effective for Concrete Durability
作者：
Liu Jiesheng* ;Li Faping;He Xiang;Liu XiaoFan;Zhang Rongtang
期刊：
MATERIALS PERFORMANCE ,2017年56(4):39-43 ISSN：0094-1492
通讯作者：
Liu Jiesheng
作者机构：
[Liu XiaoFan; Li Faping; Liu Jiesheng; He Xiang; Zhang Rongtang] Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan Changqing Pk Xuefu Southern Rd 68, Wuhan 430023, Hubei Province, Peoples R China.
通讯机构：
[Liu Jiesheng] W;Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan Changqing Pk Xuefu Southern Rd 68, Wuhan 430023, Hubei Province, Peoples R China.
摘要：
This article assesses the behavior of concrete coated with a silicone-based material. Studies were conducted to evaluate the rate of carbonation, resistance to chloride penetration, and water permeability of concrete when treated with silicone coatings. The results indicate that the water absorption, chloride ion, and carbonation resistance of concrete with a silane coating were greatly improved when compared to concrete coated with the acrylic coating used in this study and uncoated concrete. The results also show that the silane coating adheres well to the concrete surface. Scanning electron microscopy was employed to investigate the interface.<br/> ©2017, National Assoc. of Corrosion Engineers International. All rights reserved.
语种：
英文
展开
Investigation of structural, morphological, and dynamic mechanical properties of unvulcanized PDMS/silica compound
作者：
Liu, J.S.;Li, F.P.;He, X.
期刊：
Materials Performance and Characterization ,2017年6(1):33-45 ISSN：2379-1365
通讯作者：
Liu, J.S.(wsljs628@yahoo.com)
作者机构：
[Li, F.P.; Liu, J.S.; He, X.] School of Civil Engineering and Architecture, Wuhan Polytechnic University, Wuhan, 430023, China
通讯机构：
School of Civil Engineering and Architecture, Wuhan Polytechnic University, Wuhan, China
关键词：
Bound rubber;Dynamic properties;Modification;Polydimethylsiloxanes (PDMS);Silica
摘要：
In this study, the interaction between the silica filler and polydimethylsiloxanes (PDMS) was investigated from the aspects of the bound rubber and morphological characterization. With special attention to the dynamic properties, the dynamic test was conducted by dynamic shear rheometer. The results show that the modified filler disperses uniformly within the PDMS matrix without aggregation and connects closely with the matrix compared to that of the unmodified fillers. Surface modification of the filler increases the bound-rubber content. The increase in silica loading leads to an increase in the silica-silica interaction and a decrease in filler-rubber interaction, which results in the aggregation of fillers and the increase of the bound-rubber content. It was apparent that storage modulus, loss modulus, and tanδof unvulcanized PDMS/filler compounds filled with treated silica filler were lower than that of the untreated silica system. Moreover, the tanδdecreases with increasing silica loading.<br/> Copyright ©2017 by ASTM International.
语种：
英文
展开
不同粒径稻壳墙体材料基本性能研究
作者：
刘杰胜;伍玲玲;丁一;王丽艳;林梓银;...
期刊：
武汉轻工大学学报 ,2017年36(3):92-95 ISSN：2095-7386
作者机构：
武汉轻工大学土木工程与建筑学院,湖北武汉,430023;[周梦林; 王丽艳; 伍玲玲; 刘杰胜; 林梓银; 丁一; 胡秋锦] 武汉轻工大学
关键词：
不同粒径稻壳;不同含量稻壳;控制变量法;墙体材料;基本性能研究
摘要：
传统墙体材料的弊端已经日益显现,而高性能的新型建筑材料的制备的需求明显增 大.将稻壳加入水泥混凝土中制备墙体材料能够实现节能减排以及变废为宝的目标,发展前 景被看好.本文利用控制变量法,从稻壳的不同粒後以及不同含量两个方面进行系统的研究,提供相应的技术来支持高性能墙体材料的制备.
语种：
中文
展开
有机硅聚合物改性水泥砂浆的基本特征研究*
作者：
刘雨霖;刘杰胜;翟经纬;李发平
期刊：
砖瓦 ,2017年(6):31-33 ISSN：1001-6945
作者机构：
武汉轻工大学土木工程与建筑学院,湖北 武汉,430023;[刘杰胜; 李发平; 翟经纬; 刘雨霖] 武汉轻工大学
会议名称：
第八届湖北省土木工程专业大学生科技创新论坛
会议时间：
2017-06-06
会议地点：
武汉
会议论文集名称：
第八届湖北省土木工程专业大学生科技创新论坛 论文集
关键词：
有机硅;水泥砂浆;抗折强度;抗压强度;稠度;缓凝时间
摘要：
采用向普通水泥砂浆中掺入KH-550有机硅的方法来对水泥砂浆进行改性,并对其稠度,抗折强度,抗压强度及凝结时间等基本性能进行了研究.研究结果表明:有机硅的掺入降低了普通水泥砂浆的抗折强度和抗压强度,使稠度变大,并延缓了普通水泥砂浆的凝结时间.
语种：
中文
展开
钠基膨润土改性水泥砂浆的基本性能研究
作者：
贠刚;刘杰胜;李发平;王桐进;翟经纬;...
期刊：
砖瓦 ,2017年(12):22-24 ISSN：1001-6945
作者机构：
武汉轻工大学土木工程与建筑学院,武汉 湖北,430023;[王桐进; 贠刚; 刘杰胜; 李发平; 刘雨霖; 翟经纬] 武汉轻工大学
关键词：
钠基膨润土;水泥砂浆;缓凝时间;吸水率;孔隙率;稠度
摘要：
采用向普通水泥砂浆中掺入钠基膨润土的方法来对水泥砂浆进行改性,并对其凝结时间、吸水率、孔隙率和砂浆稠度等基本性能进行了研究.研究结果表明,钠基膨润土的掺入会增大砂浆孔隙率,减小吸水率和稠度,并缩短其凝结时间.
语种：
中文
展开
Study of the mechanical and physical performance of phase change materials-based cement mortar
作者：
Yu, Yuan-Yuan* ;Liu, Jie-Sheng;Lin, Zi-Yin;Wang, Yan-Li;He, Xiang
作者机构：
[He, Xiang; Yu, Yuan-Yuan; Wang, Yan-Li; Lin, Zi-Yin; Liu, Jie-Sheng] Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan 430023, Peoples R China.
会议名称：
International Conference on Advanced Materials and Energy Sustainability (AMES)
会议时间：
MAY 27-29, 2016
会议地点：
Wuhan, PEOPLES R CHINA
会议主办单位：
[Yu, Yuan-Yuan;Liu, Jie-Sheng;Lin, Zi-Yin;Wang, Yan-Li;He, Xiang] Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan 430023, Peoples R China.
关键词：
Phase change materials;physical properties;mortar
摘要：
This paper studies the mixture of cement mortar with a phase change material (PCM) and analyzes the changes in mechanical and physical performances. The experimental results demonstrate that an increase in PCM content results in decreases in consistency, compressive strength, bulk density and water retention. Therefore, these results can provide a reference for the application of phase change materials in practical engineering conditions.
语种：
英文
展开
钠基膨润土改性水泥砂浆制备与基本性能研究
作者：
刘杰胜;周梦林;胡秋锦;王丽艳;林梓银;...
期刊：
武汉轻工大学学报 ,2017年36(4):45-47,90 ISSN：2095-7386
作者机构：
武汉轻工大学土木工程与建筑学院,湖北武汉,430023;[伍玲玲; 王丽艳; 周梦林; 刘杰胜; 林梓银; 丁一; 胡秋锦] 武汉轻工大学
关键词：
钠基膨润土;水泥砂浆;基本物理性能
摘要：
通过试验在水泥砂浆中掺入不同掺量比的钠基膨润土,研究了钠基膨润土对水泥砂浆硬化后的基本物理性质.结果表明:随钠基膨润土掺量的增大,掺入钠基膨润土的水泥砂浆抗压抗折强度都呈现出减小的趋势;水泥砂浆硬化后的吸水率与钠基膨润土的掺入量成正比;钠基膨润土掺量增大,水泥砂浆试样干密度随之减小.
语种：
中文
展开
高吸水树脂改性水泥砂浆的制备及性能研究
作者：
李发平;刘杰胜;余媛媛;刑珊珊;张旭斌
期刊：
中国建筑防水 ,2017年(16):8-11 ISSN：1007-497X
作者机构：
武汉轻工大学土木工程与建筑学院,湖北武汉,430023;[刘杰胜; 李发平; 余媛媛; 刑珊珊; 张旭斌] 武汉轻工大学
关键词：
刚性防水材料;水泥砂浆;高吸水树脂;抗渗性能;早期抗裂性能
摘要：
在水泥砂浆中掺加高吸水树脂（SAP）制备刚性防水材料,以SAP作为变量,研究其对水泥砂浆流动性、湿密度、保水率、抗渗性能、抗裂性能的影响。结果表明:随着SAP掺量的增加,SAP改性水泥砂浆的流动度增大,湿密度和保水率有所降低;内掺SAP可显著提高水泥砂浆的抗渗性能和早期抗裂性能。
语种：
中文
展开
改性稻壳水泥砂浆的性能研究
作者：
左洁;董莪;刘杰胜
期刊：
砖瓦 ,2016年(6):18-19 ISSN：1001-6945
作者机构：
武汉轻工大学土木工程与建筑学院,湖北 武汉,430023;[刘杰胜; 左洁; 董莪] 武汉轻工大学
关键词：
改性稻壳;绿色资源;性能
摘要：
稻壳作为大宗废料处理是一种浪费,研究稻壳的潜在价值将其作为一种绿色资源具有重要的社会意义。主要研究改性稻壳水泥砂浆的宏观物理性能。通过试验得出,掺入不同量的改性稻壳对水泥砂浆的孔隙率、吸水率、稠度、保水率有不同程度的影响。
语种：
中文
展开
高吸水树脂水泥砂浆的基本性能研究
作者：
余媛媛;刘杰胜;邢珊珊;左洁
期刊：
中国建筑防水 ,2016年(8):1-3 ISSN：1007-497X
作者机构：
武汉轻工大学土木工程与建筑学院,湖北 武汉,430023;[刘杰胜; 左洁; 余媛媛; 邢珊珊] 武汉轻工大学
关键词：
刚性自防水材料;高吸水树脂;水泥砂浆;干制品密度;吸水率;抗压强度;抗折强度
摘要：
高吸水树脂（SAP）是一种具有超强吸水、保水能力的新型功能高分子材料,可作为水泥基材料的内养护剂制备整体刚性自防水材料。本研究通过在水泥砂浆中掺入不同比例的SAP来研究其对水泥砂浆基本性能的影响。结果表明,随着SAP掺量的增加,水泥砂浆的干制品密度、抗压强度和抗折强度降低,但吸水率升高。
语种：
中文
展开
绿色建筑建设及发展研究
作者：
黄旭;刘杰胜
期刊：
时代报告(奔流) ,2016年(2):298-298 ISSN：1003-2738
作者机构：
湖北省建筑科学研究设计院;武汉轻工大学土建学院
关键词：
绿色建筑;能耗;发展趋势
摘要：
本文简述了绿色建筑定义和作用，分析了我国绿色建筑发展不足，并指出了我国绿色建筑未来发展趋势。
语种：
中文
展开
Properties of polymer-modified mortar using silane as an integral additive
作者：
Liu, Jiesheng* ;Liu, Ke;Zhang, Juan;Li, Jixiang
期刊：
JOURNAL OF TESTING AND EVALUATION ,2016年44(1):175-182 ISSN：0090-3973
通讯作者：
Liu, Jiesheng
作者机构：
[Zhang, Juan; Liu, Jiesheng; Li, Jixiang; Liu, Ke] Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan 430023, Peoples R China.
通讯机构：
[Liu, Jiesheng] W;Wuhan Polytech Univ, Sch Civil Engn & Architecture, Wuhan 430023, Peoples R China.
关键词：
silane mortar;chloride;water abosorption;carbonation
摘要：
In the present paper, the addition of silane to improve the properties of mortar was experimentally investigated. The morphology and microstructure of mortar were investigated by using both scanning electron microscopy (SEM) and polarizing microscopy (PM). The results show that silane significantly alters the microstructure of mortar, reduces the crystallization, restricts the degree of hydration of cement-based materials, and decreases micro-voids. As a result, silane effectively improves the chemical and carbonation resistance, as well as the chloride and water penetration resistance of mortar. Results also indicate that the consistency of mortar was improved but the compressive strength of the mortar was decreased. Specifically, silane would also be beneficial to the bridging cracking function to resist crack propagation.
语种：
英文
展开
稻壳灰水泥砂浆的制备及其性能研究
作者：
邢珊珊;董莪;刘杰胜
期刊：
砖瓦 ,2016年(3):15-16 ISSN：1001-6945
作者机构：
武汉轻工大学土木工程与建筑学院,湖北 武汉,430023;[刘杰胜; 董莪; 邢珊珊] 武汉轻工大学
关键词：
稻壳灰;基本物理性能;环保
摘要：
作为一种具有潜在资源属性的废弃物,稻壳灰的综合利用具有重要的环保意义和经济效益.研究了以不同煅烧温度下的稻壳灰,制备水泥砂浆,并分析了该水泥砂浆的基本物理性能.研究结果表明:随着稻壳灰制备温度的升高,稻壳灰水泥砂浆的抗压强度降低,干密度降低,吸水率增加.
语种：
中文
展开